阻燃, 玻璃纤维增强材料30%,高强度, 抗溶解性,脱模性能良好, 汽车的发动机罩下的零件

 

Radici Compounds N66G30HSL V0 BK

聚酰胺66

Radici Plastics USA, Inc.

Technical Data

 

产品说明

 

N66G30HSL V0 BK is a nylon 6.6 compound, reinforced with 30% glass fiber, heat stabilized and flame retarded to meet the V-0 requirement of Underwriters Laboratories Standard UL94 at 0.75mm.

 

Typical of semi-crystalline polymers, glass fiber reinforced nylons exhibit outstanding resistance even at elevated temperatures to the effects of a wide range of chemicals, solvents, oils and greases and are therefore suitable for use in many harsh environments including automotive under-hood. This compound is recommended for use in applications where high strength and rigidity characteristics are required, especially if performance at high temperature is critical, combined with flame retardance.

 

N66G30HSL V0 BK is internally lubricated for improved mold release. Particular attention should be paid to processing conditions and mold design to minimize both the risk of glass fiber breakage to fully realize mechanical performance, and also abrasive wear to machine and mold. Due to the excellent high temperature rigidity of this compound, fast cycle times can be expected.

 

The test specimens were tested at 73°F and 50% relative humidity and contain less than 0.2% moisture as a result of being stored in a moisture proof container immediately after molding.

 

总体

 

材料状态 • 已商用：当前有效

资料 1 •  Processing - MDE PA66 (English)

搜索 UL 黄卡 •  Radici Plastics USA, Inc.

供货地区 • 北美洲

填料/增强材料 • 玻璃纤维增强材料, 30% 填料按重量

添加剂 • 热稳定剂 • 润滑剂 • 阻燃

• 半结晶 • 耐化学性良好 • 热稳定性，良好

• 刚性，高 • 耐热性，高

• 生产阶段，快

性能特点 • 高强度 • 耐油性能

• 脱模性能良好

• 经润滑 • 耐油脂性能

• 阻燃性能

• 抗溶解性 • 热稳定性

用途 • 汽车的发动机罩下的零件

外观 • 黑色 • 可用颜色

形式 • 颗粒料

加工方法 • 注射成型

 

物理性能 额定值单位制 测试方法

比重 1.60g/cm³ ASTM D792

收缩率 - 流动 (3.18 mm) 0.20 到 0.40% ASTM D955

吸水率 (24 hr) 0.60% ASTM D570

机械性能 额定值单位制 测试方法

抗张强度 3 (屈服, 23°C, 3.18 mm) 159MPa ASTM D638

伸长率 3 (断裂, 23°C, 3.18 mm) 3.0% ASTM D638

弯曲模量 (23°C) 8960MPa ASTM D790

弯曲强度 (23°C) 228MPa ASTM D790

冲击性能 额定值单位制 测试方法

悬壁梁缺口冲击强度 (23°C, 3.18 mm) 80J/m ASTM D256

热性能 额定值单位制 测试方法

热变形温度 (1.8 MPa, 未退火) 250°C ASTM D648

熔融温度 250 到 265°C

可燃性 额定值单位制 测试方法

UL 阻燃等级 (0.750 mm, BK) V-0 UL 94

补充信息

Elongation at Break, ASTM D638, Type I, 0.125", 73°F: 2-4 %

 

 

 

 